E-Leather has been tested extensively to determine the ultimate performance of the material. This confirms a factor of safety as high as 5 times above the specifications for some products.

Designed and developed to overcome the weaknesses of traditional leather and textiles, E-Leather is engineered to provide a range of materials that meet specific performance criteria.

PRODUCT DATA SHEET FOR SL2

TestsTest MethodTypical Values
Average thickness BS EN ISO 2589:2002 1.0-1.2mm
Width Measure on final inspection 1400mm ± 20mm
Softness IUP 36 ≥3.2
Colour measurement EL-LSTP-0004  
TestsTest MethodTypical Values
Bally flex BS EN ISO 5402:2002 Dry 50,000 cycles
Tensile strength BS EN ISO 3376:2002 * ≥10N/mm
Abrasion Resistance
(Taber)
BS EN ISO 5470-1:1999 Part 1 CS10 Wheels, 1kg, 1000cycles no
worse than slight damage of finish
and min grade 3 colour change
TestsTest MethodTypical Values
Horizontal Burn Directive 95/28/EC Annex IV †:
Horizontal Burn Test
Pass
Horizontal Burn FMVSS302 (10-1-91 Edition) Pass
Chrome VI DIN 53314 E <3mg/kg
pH EN ISO 4045 3.30~5.00
Formaldehyde DIN 53315 Part B ≤80ppm
Pentachlorophenol DIN 53313 (BLC ID-149) ND (<3mg/kg)
Azo Dyestuffs LMBG No B82.02-3 §35 ND (<30ppm)

FINGERPRINT TESTS

TestsTest MethodTypical Values
Average thickness BS EN ISO 2589:2002 1.0-1.2mm
Width Measure on final inspection 1400mm ± 20mm
Softness IUP 36 ≥3.2
Colour measurement EL-LSTP-0004  

QUALITY PERFORMANCE TESTS

TestsTest MethodTypical Values
Bally flex BS EN ISO 5402:2002 Dry 50,000 cycles
Tensile strength BS EN ISO 3376:2002 * ≥10N/mm
Abrasion Resistance
(Taber)
BS EN ISO 5470-1:1999 Part 1 CS10 Wheels, 1kg, 1000cycles no
worse than slight damage of finish
and min grade 3 colour change

FLAMMABILITY & RESTRICTED SUBSTANCE TESTS

TestsTest MethodTypical Values
Horizontal Burn Directive 95/28/EC Annex IV †:
Horizontal Burn Test
Pass
Horizontal Burn FMVSS302 (10-1-91 Edition) Pass
Chrome VI DIN 53314 E <3mg/kg
pH EN ISO 4045 3.30~5.00
Formaldehyde DIN 53315 Part B ≤80ppm
Pentachlorophenol DIN 53313 (BLC ID-149) ND (<3mg/kg)
Azo Dyestuffs LMBG No B82.02-3 §35 ND (<30ppm)

* Procedure as per BS EN ISO 3376:2002, except it is not corrected for thickness as this is not applicable to E-leather

PRODUCT DATA SHEET FOR SL4TFL

TestsTest MethodTypical Values
Average thickness BS EN ISO 2589:2002 1.1-1.3mm
Width Measure on final inspection 1400mm ± 20mm
Softness IUP 36 ≥3.2
Colour measurement EL-LSTP-0004
TestsTest MethodTypical Values
Bally flex BS EN ISO 5402:2002 Dry 50,000 cycles
Tensile strength BS EN ISO 3376:2002 * ≥10N/mm
Breaking elongation BS EN ISO 3376:2002 ≥ 20%
Abrasion Resistance
(Taber)
BS EN ISO 5470-1:1999 Part 1 CS10 Wheels, 1kg, 1000cycles no
worse than slight damage of finish
and min grade 3 colour change
TestsTest MethodTypical Values
Flammability BS5852-2:2006-Crib 7 Pass
Chrome VI DIN 53314 E <3mg/kg
pH EN ISO 4045 3.30~5.00
Formaldehyde DIN 53315 Part B ≤80ppm
Pentachlorophenol DIN 53313 (BLC ID-149) ND (<3mg/kg)
Azo Dyestuffs LMBG No B82.02-3 §35 ND (<30ppm)

FINGERPRINT TESTS

TestsTest MethodTypical Values
Average thickness BS EN ISO 2589:2002 1.1-1.3mm
Width Measure on final inspection 1400mm ± 20mm
Softness IUP 36 ≥3.2
Colour measurement EL-LSTP-0004

QUALITY PERFORMANCE TESTS

TestsTest MethodTypical Values
Bally flex BS EN ISO 5402:2002 Dry 50,000 cycles
Tensile strength BS EN ISO 3376:2002 * ≥10N/mm
Breaking elongation BS EN ISO 3376:2002 ≥ 20%
Abrasion Resistance
(Taber)
BS EN ISO 5470-1:1999 Part 1 CS10 Wheels, 1kg, 1000cycles no
worse than slight damage of finish
and min grade 3 colour change

FLAMMABILITY & RESTRICTED SUBSTANCE TESTS

TestsTest MethodTypical Values
Flammability BS5852-2:2006-Crib 7 Pass
Chrome VI DIN 53314 E <3mg/kg
pH EN ISO 4045 3.30~5.00
Formaldehyde DIN 53315 Part B ≤80ppm
Pentachlorophenol DIN 53313 (BLC ID-149) ND (<3mg/kg)
Azo Dyestuffs LMBG No B82.02-3 §35 ND (<30ppm)

* Procedure as per BS EN ISO 3376:2002, except it is not corrected for thickness as this is not applicable to E-leather